ASTM A193 B8M Class 2
ASTM A320 B8M Class 2
ASME SA193 B8M Class 2
ASME SA320 B8M Class 2
UNS S31600 Strain Hardened
316 Strained Hardened
Base Element Fe(Iron)
Element | Min | Max |
---|---|---|
C (Carbon) | 0.08% | |
Cr (Chromium) | 16% | 18% |
Mn (Manganese) | 2% | |
Mo (Molybdenum) | 2% | 3% |
Ni (Nickel) | 10% | 14% |
P (Phosphorus) | 0.045% | |
S (Sulphur) | 0.03% | |
Si (Silicon) | 1% |
Mechanical Property | Min | Max | |
---|---|---|---|
Ultimate Tensile Strength (UTS) | 760 Mpa | ||
0.2% Proof Stress | 665 Mpa | ||
Elongation (4D) | 15% | ||
Reduction of Area | 45% | ||
Hardness (Brinell) | 321 HB | ||
Hardness (Rockwell C) | 35 HRC |
Heat Treated with a carbide solution and strain hardened.
Bolting for pressure vessels, valves, flanges and fittings for high temperature or high pressure services, as well as other special purpose applications.