X3CrNiMoAl13.8.2 – Precipitation age hardened Steel

X3CrNiMoAl13.8.2 is a precipitation age hardened steel, that offers a high toughness and strength as well as a good resistance to stress corrosion cracking!

Alias

X3CrNiMoAl13.8.2
1.4534LW
XM13
S13800
SA705

Chemistry

Element Min Max
Al (Aluminium) 1.1%
C (Carbon) 0.03%
Cr (Chromium) 12.7
Mn (Manganese) 0.06%
Mo (Molybdenum) 2.2%
Ni (Nickel) 8.2%
Si (Silicon) 0.04%

Mechanical Properties Min Max
Ultimate Tensile Strength (UTS) 1210 MPa
0.2% Proof Stress 1140 MPa
Elongation 12%
Gauge Length A5D
Hardness (Rockwell C) 40 HRC 45 HRC
Charpy V-Notch Impact = Room Temp. 54 Joules

Applications

Used within the Aerospace, petrochemical and nuclear industries for applications such as aircraft components, shafts, valves etc.

Disclaimer:
Information is given for illustrative purposes only. Tachart accepts no responsibility for the accuracy of the data contained within or the use of the data by any other party.
This page is protected by copyright and may be freely distributed but not reproduced without permission.

error: Content is Copyright Tachart Bolt & Nut Manufacturing !!